VERBATIM 3D Printer Filament PMMA DURABIO 1.75mm, 159m, 500g white


VERBATIM 3D Printer Filament PMMA DURABIO 1.75mm, 159m, 500g white
TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL 9003 Weight 500 g Color white MATERIAL PROPERTIES Density 1.31 g/cm3 (Test method: ISO 1183) MVR 230°C/2.16 kg 10 cm3/10min (ISO 1133) MFR 230°C/2.16 kg 13 gr/10 min (Test method: ISO 1133) Elongation at break 130% (Test method: ISO 527) Tensile strength 64 MPa (Test method: ISO 527) Tensile modulus 2300MPa (Test method: ISO 527) Flexural modulus 2100MPa (Test method: ISO 178) Flexural strength 94 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 9 kJ/m2 (Test method: ISO 179) Moisture absorption 0.2% (Test method: MCC Method) Coefficient of linear thermal expansion (-20~80°C) 7.3E-05 (Test method: ISO 11359-2) Heat deflection temperature 1.80 MPa 82°C (Test metod: ISO 75-1) Transparency 2% (Test method: ISO 13468) RECOMMENDED PRINTER SET UP Extrusion temperature 225 - 245°C Melting temperature 235°C Bed temperature 85°C Printing speed 50 mm/s Fan speed (can be changed to 0% is the model is warping) 10% .

Podobné produkty



1227 CZK  0% 

TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL 9003 Weight 500 g Color white MATERIAL PROPERTIES Density 1.31 g/cm3 (Test method: ISO 1183) MVR 230°C/2.16 kg 10 cm3/10min (ISO 1133) MFR 230°C/2.16 kg 13 gr/10 min (Test method: ISO 1133) Elongation at break 130% (Test method: ISO 527) Tensile strength 64 MPa (Test method: ISO 527) Tensile modulus 2300MPa (Test method: ISO 527) Flexural modulus 2100MPa (Test method: ISO 178) Flexural strength 94 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 9 kJ/m2 (Test method: ISO 179) Moisture absorption 0.2% (Test method: MCC Method) Coefficient of linear thermal expansion (-20~80°C) 7.3E-05 (Test method: ISO 11359-2) Heat deflection temperature 1.80 MPa 82°C (Test metod: ISO 75-1) Transparency 2% (Test method: ISO 13468) RECOMMENDED PRINTER SET UP Extrusion temperature 225 - 245°C Melting temperature 235°C Bed temperature 85°C Printing speed 50 mm/s Fan speed (can be changed to 0% is the model is warping) 10% .